Materials/Polymers/High-performance
PEEK
misse2-peekIn short
On the International Space Station's forward-facing side, oxygen atoms ate away 252 µm of PEEK in 3.95 years, about 64 µm a year. A standard 25 µm film of it would last about 5 months there. It resists atomic oxygen 1.0 times better than Kapton H, the reference film.
Benchmarks
The benchmarks that matter for this material's applications, each compared with the reference engineers use.
| Benchmark | Result | Compared with reference |
|---|---|---|
| Atomic oxygen erosionHow fast low-orbit oxygen eats the surface. Lower is better. | 2.99×10⁻²⁴ cm³/atomLow Earth orbit, 3.95 years in flight | 1.00× Kapton HResists 1.0× better |
Not measured yet (3): darkening under UV and particles (Δα); outgassing, total mass loss (TML); thermal cycling survival.
Applications
Where materials like PEEK are considered, the benchmarks that decide each use, and what the measured data says so far.
| Application | Deciding benchmarks | What the data says |
|---|---|---|
| External surfaces in low Earth orbit1 of 2 deciding benchmarks measured |
| Atomic oxygen resistance is poor (1.00×): unprotected, it wears through quickly on forward-facing low-orbit surfaces and would need a protective coating. Still needed: darkening under UV and particles (Δα). |
"What the data says" is Space Mushroom's reading of the measured values, not a flight qualification. Deciding benchmarks come from the Benchmark Framework.
What it went through
| Where | ISS, MISSE 2, PEC 2 tray 1 (outside the Quest airlock) |
|---|---|
| When | 2001-08-16 to 2005-07-30 (3.95 years) |
| Atomic oxygen dose | 8.43×10²¹ atoms/cm² |
| Sunlight | 5,000–6,700 equivalent sun hours |
| Temperature | Cycled between −30 °C and 40 °C |
| Also exposed to | Solar UV and charged particle radiation, in vacuum |
How it compares
Materials flown on the same tray, ranked from least to most eroded. PEEK is number 24 of 40.
| Rank | Material | Compared with Kapton H | Lost in 3.95 years |
|---|---|---|---|
| 5 | FEPFluorinated ethylene propylene | 0.067× | 17 µm |
| 22 | Kapton HNPolyimide (PMDA) | 0.94× | 237 µm |
| 23 | PSUPolysulphone | 0.98× | 248 µm |
| 24 | PEEKPolyetheretherketone | 1.00× | 252 µm |
| 25 | Kapton HPolyimide (PMDA) | 1.00× | 253 µm |
| 26 | MylarPolyethylene terephthalate | 1.00× | 254 µm |
How the numbers are calculated
- Erosion yield is NASA's measurement: volume of material removed per oxygen atom.
- Thickness lost = erosion yield × oxygen dose = 2.99×10⁻²⁴ cm³/atom × 8.43×10²¹ atoms/cm² = 0.0252 cm = 252 µm.
- Compared with Kapton H = erosion yield ÷ 3.00×10⁻²⁴ (Kapton H's value on the same flight).
- Film life = 25 µm ÷ 64 µm per year, for the same exposure.
Full record
The complete spore, as stored. Free to reuse under CC-BY-4.0.
spore: passport
id: misse2-peek
spore_version: 0.1
status: measured
org: nasa
dataset: misse2-peace
material:
name: "Polyetheretherketone"
abbreviation: "PEEK"
family: Other polymer
category: polymers
type: high-performance
tags:
environments: [low-earth-orbit]
stresses: [atomic-oxygen, uv, total-radiation-dose, thermal-cycling, vacuum-and-outgassing]
applications: []
exposures:
- environment: low Earth orbit
platform: ISS, MISSE 2, PEC 2 tray 1 (outside the Quest airlock)
start: 2001-08-16
end: 2005-07-30
duration_years: 3.95
atomic_oxygen_fluence: {value: 8.43e21, unit: atoms/cm2}
solar_exposure: {value: "5000-6700", unit: equivalent sun hours}
thermal_cycling: {min_c: -30, max_c: 40, note: nominal base-plate range}
results:
- property: atomic oxygen erosion yield
value: 2.99e-24
unit: cm3/atom
lower_bound: false
sources:
- title: Atomic Oxygen Erosion Yield Predictive Tool for Spacecraft Polymers in Low Earth Orbit
id: NASA/TM-2008-215490 (Banks, Backus and de Groh, December 2008)
url: https://ntrs.nasa.gov/citations/20090011780
where: Table I; exposure details in section 2.1
license: CC-BY-4.0
Sources
- Atomic Oxygen Erosion Yield Predictive Tool for Spacecraft Polymers in Low Earth Orbit. NASA/TM-2008-215490 (Banks, Backus and de Groh, December 2008), Table I; exposure details in section 2.1.