  "spore": "profile",
  "id": "miralon-cnt-yarn",
  "spore_version": "0.2",
  "family": "carbon-materials",
  "name": "MIRALON carbon nanotube yarn and sheet",
  "abbreviation": "CNT yarn",
  "role": "Macroscopic carbon nanotube yarn and sheet, sold by Huntsman as MIRALON",
  "category": "carbon",
  "type": "nanotubes",
  "summary": "MIRALON carbon nanotube yarn and sheet is a Huntsman product made of aligned carbon nanotube filaments. Per the Perigee Direct product page, the high-strength yarn has a typical density of 0.8 g/cm3 and a typical tensile strength of 1040 MPa; the page says these typical values are not a product specification. Huntsman states that MIRALON sheets gave electrostatic discharge (ESD) protection on NASA's Juno spacecraft on its way to Jupiter, a manufacturer claim with no flight data in the pages read.",
  "best_for": "Lightweight conductive yarn that must be stitched, woven or braided; the high-strength yarn has a typical specific electrical conductivity of 18230 S*cm2/g at 20 °C per Perigee Direct.",
  "weakest_at": "Tensile strength depends on the grade: base yarn is 240 MPa and high-strength yarn is 1040 MPa, both typical values from Perigee Direct, while the NRO report gives 3 GPa for research spun yarns. These are different products and tests, so the figures are not interchangeable.",
  "identity": {
    "formula": "C (yarn of millions of aligned carbon nanotube filaments; the Huntsman page calls them structured carbon)",
    "cas": "",
    "crystal_system": "",
    "space_group": "",
    "designations": [
      {
        "system": "Trade name",
        "code": "MIRALON",
        "source": "miralon-huntsman",
        "where": "Page title and Products heading, 'MIRALON Carbon Nanotube Materials'"
      }
    ],
    "source": "miralon-huntsman",
    "where": "Product description: MIRALON yarn products are carbon-based fibres composed of millions of aligned filaments of structured carbon"
  },
  "tags": {
    "environments": [],
    "stresses": [],
    "applications": [
      "structures",
      "electronics-and-chips"
    ]
  },
  "properties": [
    {
      "benchmark": "density",
      "label": "Density, base yarn",
      "value": 0.6,
      "bound": "exact",
      "unit": "g/cm3",
      "scope": "material",
      "conditions": {
        "yarn": "base yarn",
        "basis": "typical production batches, standard test methods; typical values only, not a product specification"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct); footnotes (1) and (2) are printed without row markers",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Density row, Base Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "density",
      "label": "Density, high-strength yarn",
      "value": 0.8,
      "bound": "exact",
      "unit": "g/cm3",
      "scope": "material",
      "conditions": {
        "yarn": "high-strength yarn",
        "basis": "typical production batches, standard test methods; typical values only, not a product specification"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct); footnotes (1) and (2) are printed without row markers",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Density row, High Strength Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "linear_density",
      "label": "Linear density, base yarn",
      "value": 10,
      "bound": "exact",
      "unit": "Tex (g/km)",
      "scope": "material",
      "conditions": {
        "yarn": "base yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct)",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Linear density row, Base Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "linear_density",
      "label": "Linear density, high-strength yarn",
      "value": 31,
      "bound": "exact",
      "unit": "Tex (g/km)",
      "scope": "material",
      "conditions": {
        "yarn": "high-strength yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct)",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Linear density row, High Strength Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "diameter",
      "label": "Diameter, base yarn",
      "value": 150,
      "bound": "exact",
      "unit": "μm",
      "scope": "material",
      "conditions": {
        "yarn": "base yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct)",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Diameter row, Base Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "diameter",
      "label": "Diameter, high-strength yarn",
      "value": 240,
      "bound": "exact",
      "unit": "μm",
      "scope": "material",
      "conditions": {
        "yarn": "high-strength yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct)",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Diameter row, High Strength Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "specific_electrical_conductivity",
      "label": "Specific electrical conductivity, base yarn",
      "value": 2840,
      "bound": "exact",
      "unit": "S*cm2/g",
      "scope": "material",
      "conditions": {
        "yarn": "base yarn",
        "temperature": "20 °C (as printed, @20°C)",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct); the row is specific, so it is per unit mass",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Specific electrical conductivity row, Base Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "specific_electrical_conductivity",
      "label": "Specific electrical conductivity, high-strength yarn",
      "value": 18230,
      "bound": "exact",
      "unit": "S*cm2/g",
      "scope": "material",
      "conditions": {
        "yarn": "high-strength yarn",
        "temperature": "20 °C (as printed, @20°C)",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct); the row is specific, so it is per unit mass",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Specific electrical conductivity row, High Strength Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "tenacity",
      "label": "Tenacity, base yarn",
      "value": 0.4,
      "bound": "exact",
      "unit": "N/Tex",
      "scope": "material",
      "conditions": {
        "yarn": "base yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct)",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Tenacity row, Base Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "tenacity",
      "label": "Tenacity, high-strength yarn",
      "value": 1.3,
      "bound": "exact",
      "unit": "N/Tex",
      "scope": "material",
      "conditions": {
        "yarn": "high-strength yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct)",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Tenacity row, High Strength Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "ultimate_tensile_strength",
      "label": "Tensile strength, base yarn (typical)",
      "value": 240,
      "bound": "exact",
      "unit": "MPa",
      "scope": "material",
      "conditions": {
        "yarn": "base yarn",
        "basis": "typical production batches, standard test methods; typical values only, not a product specification"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct); test method not named on the page",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Tensile strength row, Base Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "ultimate_tensile_strength",
      "label": "Tensile strength, high-strength yarn (typical)",
      "value": 1040,
      "bound": "exact",
      "unit": "MPa",
      "scope": "material",
      "conditions": {
        "yarn": "high-strength yarn",
        "basis": "typical production batches, standard test methods; typical values only, not a product specification"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct); test method not named on the page",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Tensile strength row, High Strength Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "elastic_modulus",
      "label": "Tensile modulus, base yarn (typical)",
      "value": 4.9,
      "bound": "exact",
      "unit": "GPa",
      "scope": "material",
      "conditions": {
        "yarn": "base yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct); test method not named on the page",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Tensile modulus row, Base Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "elastic_modulus",
      "label": "Tensile modulus, high-strength yarn (typical)",
      "value": 46.4,
      "bound": "exact",
      "unit": "GPa",
      "scope": "material",
      "conditions": {
        "yarn": "high-strength yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct); test method not named on the page",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Tensile modulus row, High Strength Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "elongation",
      "label": "Strain at break, base yarn (typical)",
      "value": 27,
      "bound": "exact",
      "unit": "%",
      "scope": "material",
      "conditions": {
        "yarn": "base yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct)",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Strain at break row, Base Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "elongation",
      "label": "Strain at break, high-strength yarn (typical)",
      "value": 3.5,
      "bound": "exact",
      "unit": "%",
      "scope": "material",
      "conditions": {
        "yarn": "high-strength yarn",
        "basis": "typical production batches; typical values only"
      },
      "method": "Typical value in the Typical Physical Properties table of a reseller product page (Perigee Direct)",
      "status": "ground",
      "source": "perigee-miralon",
      "where": "Typical Physical Properties table, Strain at break row, High Strength Yarn column",
      "source_detail": {
        "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
        "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
        "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
        "kind": "datasheet",
        "license": "Reseller product page, cited and not reproduced"
      }
    },
    {
      "benchmark": "ultimate_tensile_strength",
      "label": "Tensile strength, spun CNT yarns (research achievement)",
      "value": 3,
      "bound": "exact",
      "unit": "GPa",
      "scope": "material",
      "conditions": {
        "form": "spun CNT yarns, research achievement; product not named in the report",
        "basis": "current achievement as printed; no test method given"
      },
      "method": "Stated as a current achievement in Table 1 of a US National Reconnaissance Office presentation hosted by nano.gov",
      "status": "ground",
      "source": "nro-cnt-yarns",
      "where": "Table 1, row Strength - Spun Yarns",
      "source_detail": {
        "title": "Carbon Nanotube Yarns and Sheets for Structural Components (National Reconnaissance Office, hosted by nano.gov)",
        "id": "NRO presentation; PDF metadata created 2010-01-21; cites Lashmore and Antoinette, 2009",
        "url": "https://www.nano.gov/sites/default/files/carbon_nanotube_yarns_and_sheets_for_structural_components-nro.pdf",
        "year": 2010,
        "kind": "report",
        "license": "US federal government document, as hosted by nano.gov"
      }
    },
    {
      "benchmark": "ultimate_tensile_strength",
      "label": "Tensile strength, CNT sheets without binders (low end of range)",
      "value": 500,
      "bound": "exact",
      "unit": "MPa",
      "scope": "material",
      "conditions": {
        "form": "CNT sheets without binders",
        "basis": "low end of the printed range, which depends on tube orientation"
      },
      "method": "Range as printed in Table 1 of a US National Reconnaissance Office presentation hosted by nano.gov; each end is recorded separately",
      "status": "ground",
      "source": "nro-cnt-yarns",
      "where": "Table 1, row Strength - Sheets",
      "source_detail": {
        "title": "Carbon Nanotube Yarns and Sheets for Structural Components (National Reconnaissance Office, hosted by nano.gov)",
        "id": "NRO presentation; PDF metadata created 2010-01-21; cites Lashmore and Antoinette, 2009",
        "url": "https://www.nano.gov/sites/default/files/carbon_nanotube_yarns_and_sheets_for_structural_components-nro.pdf",
        "year": 2010,
        "kind": "report",
        "license": "US federal government document, as hosted by nano.gov"
      }
    },
    {
      "benchmark": "ultimate_tensile_strength",
      "label": "Tensile strength, CNT sheets without binders (high end of range)",
      "value": 1.2,
      "bound": "exact",
      "unit": "GPa",
      "scope": "material",
      "conditions": {
        "form": "CNT sheets without binders",
        "basis": "high end of the printed range, which depends on tube orientation"
      },
      "method": "Range as printed in Table 1 of a US National Reconnaissance Office presentation hosted by nano.gov; each end is recorded separately",
      "status": "ground",
      "source": "nro-cnt-yarns",
      "where": "Table 1, row Strength - Sheets",
      "source_detail": {
        "title": "Carbon Nanotube Yarns and Sheets for Structural Components (National Reconnaissance Office, hosted by nano.gov)",
        "id": "NRO presentation; PDF metadata created 2010-01-21; cites Lashmore and Antoinette, 2009",
        "url": "https://www.nano.gov/sites/default/files/carbon_nanotube_yarns_and_sheets_for_structural_components-nro.pdf",
        "year": 2010,
        "kind": "report",
        "license": "US federal government document, as hosted by nano.gov"
      }
    },
    {
      "benchmark": "tenacity",
      "label": "Tenacity, as-received Miralon yarn (large cross-section yarn, LCY)",
      "value": 0.911,
      "bound": "exact",
      "unit": "N/tex",
      "scope": "material",
      "conditions": {
        "yarn": "as-received Miralon yarn from Nanocomp Technologies (LCY); grade not stated",
        "gauge_length": "100 to 120 mm",
        "loading": "capstan grips, 3 N/min loading rate, preload 0.1 to 0.15 N",
        "basis": "average of the tested samples; spread printed as plus or minus 0.137"
      },
      "method": "Average specific tensile strength from Table 1 of a 2020 SAMPE paper by the High-Performance Materials Institute, Florida A&M University and Florida State University; specific stress calculated from the average linear density",
      "status": "ground",
      "note": "A research test at 100 to 120 mm gauge length, per tex. It is not the same test or grade as the Perigee Direct tenacity rows above, which are reseller typical values.",
      "source": "sampe-cnt-yarn",
      "where": "Table 1, row LCY, Avg. Specific Tensile Strength column",
      "source_detail": {
        "title": "Tensile strength and failure modes of continuous carbon nanotube yarns for structural composite application (SAMPE Virtual Conference Proceedings, 2020)",
        "id": "SAMPE TP20-0000000156; Dessureault et al., High-Performance Materials Institute, Florida A&M University - Florida State University",
        "url": "https://www.digitallibrarynasampe.org/data/pdfs/s2020_pdfs/TP20-0000000156.pdf",
        "year": 2020,
        "kind": "paper",
        "license": "SAMPE copyright, cited and not reproduced"
      }
    },
    {
      "benchmark": "specific_stiffness",
      "label": "Specific stiffness, as-received Miralon yarn (LCY)",
      "value": 46.845,
      "bound": "exact",
      "unit": "N/tex",
      "scope": "material",
      "conditions": {
        "yarn": "as-received Miralon yarn from Nanocomp Technologies (LCY); grade not stated",
        "gauge_length": "100 to 120 mm",
        "loading": "capstan grips, 3 N/min loading rate, preload 0.1 to 0.15 N",
        "basis": "average of the tested samples; spread printed as plus or minus 9.778"
      },
      "method": "Average specific stiffness from Table 1 of the same 2020 SAMPE paper",
      "status": "ground",
      "source": "sampe-cnt-yarn",
      "where": "Table 1, row LCY, Avg. Specific Stiffness column",
      "source_detail": {
        "title": "Tensile strength and failure modes of continuous carbon nanotube yarns for structural composite application (SAMPE Virtual Conference Proceedings, 2020)",
        "id": "SAMPE TP20-0000000156; Dessureault et al., High-Performance Materials Institute, Florida A&M University - Florida State University",
        "url": "https://www.digitallibrarynasampe.org/data/pdfs/s2020_pdfs/TP20-0000000156.pdf",
        "year": 2020,
        "kind": "paper",
        "license": "SAMPE copyright, cited and not reproduced"
      }
    },
    {
      "benchmark": "elongation",
      "label": "Failure strain, as-received Miralon yarn (LCY)",
      "value": 3.186,
      "bound": "exact",
      "unit": "%",
      "scope": "material",
      "conditions": {
        "yarn": "as-received Miralon yarn from Nanocomp Technologies (LCY); grade not stated",
        "gauge_length": "100 to 120 mm",
        "loading": "capstan grips, 3 N/min loading rate, preload 0.1 to 0.15 N",
        "basis": "average of the tested samples; spread printed as plus or minus 0.632"
      },
      "method": "Average failure strain from Table 1 of the same 2020 SAMPE paper",
      "status": "ground",
      "source": "sampe-cnt-yarn",
      "where": "Table 1, row LCY, Avg. Failure Strain column",
      "source_detail": {
        "title": "Tensile strength and failure modes of continuous carbon nanotube yarns for structural composite application (SAMPE Virtual Conference Proceedings, 2020)",
        "id": "SAMPE TP20-0000000156; Dessureault et al., High-Performance Materials Institute, Florida A&M University - Florida State University",
        "url": "https://www.digitallibrarynasampe.org/data/pdfs/s2020_pdfs/TP20-0000000156.pdf",
        "year": 2020,
        "kind": "paper",
        "license": "SAMPE copyright, cited and not reproduced"
      }
    }
  ],
  "corrosion": [],
  "risks": {
    "hazards": [
      {
        "text": "There are no UK statutory workplace exposure limits (WELs) specifically for nanomaterials, according to HSE.",
        "ghs": [],
        "source": "hsg272",
        "where": "Workplace exposure limits, paragraph 25"
      },
      {
        "text": "CNTs may be pure carbon or contain metals or residual catalyst. Long straight fibres should be assumed to have the potential to cause the health effects HSE identifies for biopersistent high aspect ratio nanomaterials, in the absence of evidence to the contrary.",
        "ghs": [],
        "source": "hsg272",
        "where": "CNTs section (page 6 of the report)"
      },
      {
        "text": "Tangled, low-density fluffy bundles have no evidence so far of a hazard for the pleural cavity, but may still cause inflammation in the lungs. HSE says it is not possible to make statements about the long-term consequences of repeated exposure to tangled CNTs.",
        "ghs": [],
        "source": "hsg272",
        "where": "CNTs section (page 6 of the report)"
      }
    ],
    "failure_risks": [
      {
        "mode": "Dust explosion of loose carbon powder",
        "trigger": "Powder mixed with air",
        "consequence": "PubChem's carbon record, citing ICSC, says dust explosions are possible when the powder is mixed with air. The note is for carbon powder, not for MIRALON yarn, and no test of MIRALON yarn was found.",
        "severity": "low",
        "source": "pubchem-carbon",
        "where": "Safety and Hazards, Dust explosion note (ICSC)"
      }
    ],
    "side_effects": [],
    "handling": [
      {
        "text": "Store in a cool, dry place, in the original package, away from direct sunlight.",
        "source": "perigee-miralon",
        "where": "Storage section"
      },
      {
        "text": "HSE advises a precautionary risk management approach when workers may inhale CNTs or other biopersistent high aspect ratio nanomaterials.",
        "source": "hsg272",
        "where": "CNTs section, precautionary approach paragraph"
      }
    ],
    "mitigations": []
  },
  "uses": [
    {
      "application": "structures",
      "device": "ESD protection layer on a composite spacecraft surface (NASA Juno, manufacturer's claim)",
      "example": "Huntsman says MIRALON sheets were used on NASA's Juno spacecraft to protect against electrostatic discharge on the way to Jupiter. The sheets were laid directly onto the composite in place of metallic solutions that are typically bonded to the surface.",
      "source": "miralon-huntsman",
      "where": "Aerospace section, paragraph on the NASA Juno spacecraft"
    },
    {
      "application": "electronics-and-chips",
      "device": "Woven CNT yarn antenna (research)",
      "example": "Figure 3 of the NRO report shows a woven CNT yarn antenna. The report says yarn applications range from mesh antenna structures and wearable electronics to conductive wiring.",
      "source": "nro-cnt-yarns",
      "where": "Figure 3 caption; Yarns paragraph"
    },
    {
      "application": "structures",
      "device": "Structural reinforcement in composites and pressure vessels",
      "example": "Perigee Direct lists structural reinforcement in composites and pressure vessels among the popular uses of the yarn. The page gives no test data for this use.",
      "source": "perigee-miralon",
      "where": "Popular Applications and Uses; Applications list"
    },
    {
      "application": "structures",
      "device": "ESD protection surface layer on Juno composite components (EMSHIELD CNT sheet, per Nanocomp's 2011 release)",
      "example": "Nanocomp's 2011 release says its EMSHIELD CNT sheet was built into the Juno spacecraft as a surface layer for electrostatic discharge protection on the way to Jupiter. The release names EMSHIELD; this profile found no source that says EMSHIELD and MIRALON are the same product.",
      "source": "nanocomp-juno-2011",
      "where": "Press release body, paragraphs on the material and its use"
    }
  ],
  "supply": [
    {
      "subject": "Feedstock: natural gas or other hydrocarbons (MIRALON process)",
      "abundance": "Not quantified on the pages read",
      "producers": [],
      "critical_lists": [],
      "substitutes": [],
      "source": "miralon-huntsman",
      "where": "Near Net-Zero Manufacturing Process section: the process takes natural gas or other hydrocarbons and separates them"
    },
    {
      "subject": "Natural graphite (closest carbon commodity; not MIRALON's feedstock)",
      "abundance": "World mine production 1,800,000 tons (2025e, rounded), up from 1,550,000 tons in 2024; world reserves 310,000,000 tons",
      "producers": [
        {
          "country": "China",
          "share_percent": 82,
          "year": 2025
        }
      ],
      "critical_lists": [],
      "substitutes": [],
      "source": "usgs-graphite-2026",
      "where": "Events, Trends and Issues (China share); World Mine Production and Reserves table (world total, rounded)"
    }
  ],
  "media": [],
  "documents": [
    {
      "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
      "type": "datasheet",
      "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549"
    },
    {
      "title": "Carbon Nanotube Yarns and Sheets for Structural Components (National Reconnaissance Office, Table 1)",
      "type": "report",
      "url": "https://www.nano.gov/sites/default/files/carbon_nanotube_yarns_and_sheets_for_structural_components-nro.pdf",
      "year": 2010
    },
    {
      "title": "MIRALON Carbon Nanotube Materials (Huntsman Corporation product page)",
      "type": "datasheet",
      "url": "https://www.miralon.com/"
    },
    {
      "title": "HSE HSG272: Using nanomaterials at work, including carbon nanotubes (CNTs) and other biopersistent high aspect ratio nanomaterials (HARNs)",
      "type": "report",
      "url": "https://www.hse.gov.uk/pubns/books/hsg272.pdf",
      "year": 2013
    },
    {
      "title": "Mineral Commodity Summaries 2026: Graphite (Natural)",
      "type": "report",
      "url": "https://pubs.usgs.gov/periodicals/mcs2026/mcs2026-graphite.pdf",
      "year": 2026
    },
    {
      "title": "PubChem compound record: Carbon, CID 5462310",
      "type": "database",
      "url": "https://pubchem.ncbi.nlm.nih.gov/compound/5462310"
    },
    {
      "title": "Tensile strength and failure modes of continuous carbon nanotube yarns for structural composite application (SAMPE 2020)",
      "type": "paper",
      "url": "https://www.digitallibrarynasampe.org/data/pdfs/s2020_pdfs/TP20-0000000156.pdf",
      "year": 2020
    },
    {
      "title": "Nanocomp Reaches New Frontiers on NASA's Juno Mission (press release, copy on aeroweb-fr)",
      "type": "report",
      "url": "https://www.aeroweb-fr.net/depeches/2011/08/nanocomp-reaches-new-frontiers-on-nasas-juno-mission",
      "year": 2011
    }
  ],
  "gaps": [
    "Thermal conductivity, electrical resistivity in ohm and a service temperature range for MIRALON were not printed on any page read. The Huntsman page calls the yarn thermally and electrically conductive without numbers.",
    "The Juno ESD use rests on Huntsman's page for MIRALON and on Nanocomp's 2011 release for EMSHIELD CNT sheet. The release names EMSHIELD, and this profile found no source that links EMSHIELD to MIRALON. No NASA, JPL or flight-data source was read, and no in-flight result was found.",
    "The SAMPE paper tested as-received Miralon yarn from Nanocomp (LCY) and does not state whether it is the base or the high-strength grade, so its values are not mapped to the Perigee rows.",
    "The Huntsman 2025 technical data sheet link redirects to a document store and was not read. A search snippet describing its figures was not used as a value.",
    "The Perigee Direct table is a reseller page with typical values for two yarn grades. The manufacturer's datasheet was not reached, and footnotes (1) and (2) are printed without row markers, so the basis of each row is not stated.",
    "The NRO report (file dated 2010, citing a 2009 talk) gives current achievements for research CNT yarns and sheets. It does not name MIRALON. Nanocomp's own product site could not be reached in this run; its 2011 Juno release was read as a copy on aeroweb-fr.",
    "Corrosion and ageing: no test data for MIRALON. Perigee Direct says the yarn does not burn, melt or corrode, with no test or condition given.",
    "Supply: no MIRALON production volume, capacity or country share was found. The graphite figures are for natural graphite, not MIRALON's feedstock, and the critical-mineral status of natural graphite was not read.",
    "Hazards: no MIRALON safety data sheet was found. The PubChem carbon record is for elemental carbon, not for CNTs or yarn, and its GHS data were not used.",
    "The Perigee claim that the yarn is up to 25 times stronger than steel (specific strength) has no test basis or table on the page, so it is not used as a value.",
    "Property names not in spores/property-canon.yaml, used as short snake_case names: specific_electrical_conductivity, tenacity, linear_density, diameter, specific_stiffness.",
    "Designations: only the trade name MIRALON is recorded. The Perigee SKU codes are vendor product codes, not grade designations."
  ],
  "story": {
    "why": "MIRALON is a carbon nanotube yarn and sheet made by Huntsman Corporation and sold in yarn form by resellers such as Perigee Direct. It matters because it has typical tensile and electrical values printed in a reseller table, and because Huntsman states that MIRALON sheets were used for electrostatic discharge protection on NASA's Juno spacecraft. The Juno use is a manufacturer statement, and no flight data was read in this run.",
    "uses": [
      {
        "where": "Spacecraft ESD protection (manufacturer's claim)",
        "line": "Huntsman says MIRALON sheets were laid directly onto a composite spacecraft structure on NASA's Juno spacecraft to protect against electrostatic discharge on the way to Jupiter. The sheets replaced metallic solutions that are typically bonded to the surface."
      },
      {
        "where": "Antennas and conductive wiring (research)",
        "line": "The NRO report shows a woven CNT yarn antenna in Figure 3. It lists mesh antenna structures and conductive wiring among yarn applications."
      },
      {
        "where": "Composites",
        "line": "Perigee Direct lists structural reinforcement in composites and pressure vessels among the yarn's popular uses. The page gives no test data for this use."
      }
    ],
    "can_do": [
      {
        "label": "Strength of the yarn",
        "line": "Base yarn has a typical tensile strength of 240 MPa and high-strength yarn 1040 MPa, per Perigee Direct's typical values table. The NRO report gives 3 GPa for research spun CNT yarns and does not name a product.",
        "benchmark": "ultimate_tensile_strength",
        "scope": "material"
      },
      {
        "label": "Electrical conduction",
        "line": "High-strength yarn has a typical specific electrical conductivity of 18230 S*cm2/g at 20 °C, against 2840 S*cm2/g for base yarn, per Perigee Direct.",
        "benchmark": "specific_electrical_conductivity",
        "scope": "material"
      },
      {
        "label": "Stiffness",
        "line": "Tensile modulus is 4.9 GPa for base yarn and 46.4 GPa for high-strength yarn, both typical values per Perigee Direct.",
        "benchmark": "elastic_modulus",
        "scope": "material"
      },
      {
        "label": "Density",
        "line": "Yarn density is typically 0.6 g/cm3 for base yarn and 0.8 g/cm3 for high-strength yarn, per Perigee Direct.",
        "benchmark": "density",
        "scope": "material"
      }
    ],
    "compare": "The NRO report lists 3 GPa for research spun CNT yarns and says aluminium breaks at 500 MPa and carbon steel at around 1 GPa. The high-strength MIRALON yarn is typically 1040 MPa on the Perigee Direct table, so the two sources do not give the same figure for a yarn product. The NRO report also says CNT yarn and sheet weigh less than half as much as aluminium, a comparison the reseller table does not make.",
    "compare_rows": [
      {
        "label": "High-strength yarn tensile strength (typical)",
        "benchmark": "ultimate_tensile_strength",
        "scope": "material"
      },
      {
        "label": "High-strength yarn density (typical)",
        "benchmark": "density",
        "scope": "material"
      },
      {
        "label": "High-strength yarn specific electrical conductivity (typical)",
        "benchmark": "specific_electrical_conductivity",
        "scope": "material"
      }
    ],
    "handling": [
      "Store in a cool, dry place, in the original package, away from direct sunlight, per the Perigee Direct storage note.",
      "Treat loose or powdered CNT material as an inhalation hazard and follow HSE's precautionary approach.",
      "Ask the supplier for the safety data sheet for the exact product, since none for MIRALON was read in this run."
    ],
    "good_for": [
      "Lightweight conductive yarn that is stitched, woven or braided, where typical conductivity and strength per unit weight matter more than the highest possible tensile figure.",
      "Electrostatic discharge layers on composite structures, following the manufacturer's Juno statement."
    ],
    "watch_out": [
      "The Perigee Direct values are typical values from a reseller, not a manufacturer specification, and the page says so.",
      "Yarn strength depends on the grade: base yarn is 240 MPa and high-strength yarn is 1040 MPa, both typical values.",
      "No corrosion, ageing, thermal or temperature-range data for MIRALON was found in the pages read.",
      "The Juno ESD use is a manufacturer statement without flight data in this profile."
    ],
    "verdict": "MIRALON is a commercial carbon nanotube yarn with typical electrical and tensile values and a manufacturer-stated spacecraft ESD use on Juno. The values come from a reseller table and a government report, so this profile stays a draft until the manufacturer datasheet and a flight source are read.",
    "recipe": {
      "line": "MIRALON yarn is made of millions of aligned filaments of structured carbon, which the Perigee Direct page describes as carbon nanotubes. The Huntsman page describes an FC-CVD manufacturing process that makes hydrogen as a by-product and a solid carbon product from natural gas or other hydrocarbons.",
      "parts": [
        {
          "name": "Carbon",
          "symbol": "C",
          "role": "The only element named for the yarn. Each nanotube wall is a rolled sheet of carbon, so the product is carbon unless catalyst or other material remains. The page does not state the residual content.",
          "atoms": 1,
          "atomic_weight": 12.011
        }
      ]
    },
    "risk_groups": [
      {
        "title": "For people",
        "lead": "HSE advises a precautionary approach for CNTs that workers may inhale, and no UK exposure limit is set for nanomaterials. No safety data sheet for MIRALON was read.",
        "points": [
          {
            "label": "Inhalation",
            "line": "Long straight CNT fibres should be assumed to carry the health effects HSE identifies for biopersistent fibres. Tangled, fluffy bundles may still cause lung inflammation."
          },
          {
            "label": "Exposure limits",
            "line": "HSE says there are no UK statutory workplace exposure limits set specifically for nanomaterials."
          },
          {
            "label": "Dust",
            "line": "PubChem's carbon record, citing ICSC, says carbon powder mixed with air can cause a dust explosion. The note is for carbon powder, not for MIRALON yarn."
          }
        ],
        "level": 1,
        "verdict": "Handle as a precaution"
      }
    ]
  },
  "updated": "2026-11-01",
  "review": {
    "status": "draft",
    "method": "assistant",
    "checked_values": 22,
    "unreachable": 0,
    "caveats": 3,
    "note": "Written by an assistant on 2026-11-01 from eight sources read in this run: the Perigee Direct product page, the NRO CNT yarn presentation, the Huntsman MIRALON page, HSE HSG272, USGS MCS 2026 graphite, the PubChem carbon record, the 2020 SAMPE paper on Nanocomp Miralon yarn (three properties) and Nanocomp's 2011 Juno press release (one use). The Perigee values are reseller typical values, not a manufacturer specification. NASA and Nanocomp's own site were not reached."
  },
  "sources": {
    "perigee-miralon": {
      "title": "Perigee Direct product page: Miralon Yarn, Thread, String, 2-ply and 4-ply (Typical Physical Properties table)",
      "id": "SKU MIRALON_YARN_2PLY_100549_001FT_SAMPLE; Y-T02C-10-4, Y-T02C-10-2, 100079, 100549",
      "url": "https://www.perigeedirect.com/products/miralon-yarn-thread-string-2ply-4ply-carbon-graphene-nanotubes-y-t02c-10-4-y-t02c-10-2-100079-100549",
      "kind": "datasheet",
      "license": "Reseller product page, cited and not reproduced"
    },
    "nro-cnt-yarns": {
      "title": "Carbon Nanotube Yarns and Sheets for Structural Components (National Reconnaissance Office, hosted by nano.gov)",
      "id": "NRO presentation; PDF metadata created 2010-01-21; cites Lashmore and Antoinette, 2009",
      "url": "https://www.nano.gov/sites/default/files/carbon_nanotube_yarns_and_sheets_for_structural_components-nro.pdf",
      "year": 2010,
      "kind": "report",
      "license": "US federal government document, as hosted by nano.gov"
    },
    "miralon-huntsman": {
      "title": "MIRALON Carbon Nanotube Materials (Huntsman Corporation product page)",
      "id": "Huntsman Corporation, MIRALON division",
      "url": "https://www.miralon.com/",
      "kind": "web",
      "license": "Manufacturer web page, cited and not reproduced"
    },
    "hsg272": {
      "title": "HSE HSG272: Using nanomaterials at work, including carbon nanotubes (CNTs) and other biopersistent high aspect ratio nanomaterials (HARNs)",
      "id": "HSE HSG272",
      "url": "https://www.hse.gov.uk/pubns/books/hsg272.pdf",
      "year": 2013,
      "kind": "report",
      "license": "HSE publication (Crown copyright), cited"
    },
    "usgs-graphite-2026": {
      "title": "Mineral Commodity Summaries 2026: Graphite (Natural)",
      "id": "USGS MCS 2026",
      "url": "https://pubs.usgs.gov/periodicals/mcs2026/mcs2026-graphite.pdf",
      "year": 2026,
      "kind": "report",
      "license": "Public domain (USGS)"
    },
    "pubchem-carbon": {
      "title": "PubChem compound record: Carbon, CID 5462310 (CAS 7440-44-0)",
      "id": "CID 5462310",
      "url": "https://pubchem.ncbi.nlm.nih.gov/compound/5462310",
      "kind": "database",
      "license": "PubChem public data"
    },
    "sampe-cnt-yarn": {
      "title": "Tensile strength and failure modes of continuous carbon nanotube yarns for structural composite application (SAMPE Virtual Conference Proceedings, 2020)",
      "id": "SAMPE TP20-0000000156; Dessureault et al., High-Performance Materials Institute, Florida A&M University - Florida State University",
      "url": "https://www.digitallibrarynasampe.org/data/pdfs/s2020_pdfs/TP20-0000000156.pdf",
      "year": 2020,
      "kind": "paper",
      "license": "SAMPE copyright, cited and not reproduced"
    },
    "nanocomp-juno-2011": {
      "title": "Nanocomp Reaches New Frontiers on NASA's Juno Mission (press release, copy on aeroweb-fr)",
      "id": "Nanocomp Technologies, Inc. press release distributed by Business Wire, 8 August 2011",
      "url": "https://www.aeroweb-fr.net/depeches/2011/08/nanocomp-reaches-new-frontiers-on-nasas-juno-mission",
      "year": 2011,
      "kind": "web",
      "license": "Press release, cited and not reproduced"
    }
  },
  "license": "CC-BY-4.0",
  "url": "https://spacemushroom.com/profiles/miralon-cnt-yarn/"
}