  "spore": "profile",
  "id": "fused-silica-optical-solar-reflector",
  "spore_version": "0.2",
  "family": "optical-coatings",
  "name": "Fused silica optical solar reflector (OSR, second-surface silver mirror)",
  "abbreviation": "OSR",
  "role": "Low-absorptance, high-emittance radiator surface for spacecraft",
  "category": "coatings",
  "type": "optical-solar-reflectors",
  "summary": "An optical solar reflector (OSR) is a second-surface silver mirror on a glass substrate, used on spacecraft radiators to reflect sunlight while radiating heat. In a 1968 Lockheed study for NASA, prepared fused silica OSRs had a solar absorptance of 0.044 on average before ultraviolet exposure, rising to 0.054 after 500 equivalent sun-hours of ultraviolet at 700 K. The same study printed a total hemispherical emittance of 0.80 at 300 K, falling to 0.67 at 750 K. A commercial SQUID3 SQ-1 OSR is listed with a solar absorptance of 0.1 and an infrared emittance above 0.8, but its datasheet does not name the substrate.\n",
  "best_for": "Spacecraft radiator surfaces that must reflect sunlight while shedding heat (low solar absorptance with high infrared emittance)",
  "weakest_at": "Unprotected silver: a bare silver film blackened within a fraction of a second in the 1968 hydrogen sulfide test, and emittance falls as the surface warms",
  "identity": {
    "formula": "Second-surface silver mirror on a fused silica substrate, optionally overcoated with alumina (aluminium oxide)",
    "designations": [],
    "source": "nasa1968",
    "where": "Section 2 (program objectives: OSR defined as a second surface mirror of silver on a fused silica substrate); Section 2.4.3 (alumina overcoat)"
  },
  "tags": {
    "environments": [],
    "stresses": [],
    "applications": [
      "thermal-control"
    ]
  },
  "properties": [
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, SQ-1 rigid OSR",
      "value": 0.1,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "product": "SQ-1 Rigid Optical Solar Reflector",
        "test": "not printed on the datasheet"
      },
      "method": "Vendor product table; the datasheet prints the value without a unit, recorded as dimensionless",
      "status": "ground",
      "source": "squid3-sq1-datasheet",
      "where": "Product table, row SQ-1, column SOLAR ABSORPTANCE (alpha)",
      "source_detail": {
        "title": "SQ-1 and SQ-2 Optical Solar Reflectors datasheet (SQUID3 Space, Version 2024/10)",
        "id": "SQUID3 datasheet, Version 2024/10; hosted on SatCatalog",
        "url": "https://satcatalog.s3.amazonaws.com/components/1449/SatCatalog_-_SQUID3_Space_-_SQ-1_Optical_Solar_Reflectors_-_Datasheet.pdf?lastmod=20260119070530",
        "year": 2024,
        "kind": "datasheet",
        "license": "vendor document, linked not reproduced"
      }
    },
    {
      "benchmark": "infrared_emittance",
      "label": "IR emittance, SQ-1 rigid OSR",
      "value": 0.8,
      "bound": "lower",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "product": "SQ-1 Rigid Optical Solar Reflector",
        "printed": "> 0.8"
      },
      "method": "Vendor product table, printed as '> 0.8' with no test method; recorded as a lower bound and dimensionless",
      "status": "ground",
      "source": "squid3-sq1-datasheet",
      "where": "Product table, row SQ-1, column IR EMITTANCE (epsilon)",
      "source_detail": {
        "title": "SQ-1 and SQ-2 Optical Solar Reflectors datasheet (SQUID3 Space, Version 2024/10)",
        "id": "SQUID3 datasheet, Version 2024/10; hosted on SatCatalog",
        "url": "https://satcatalog.s3.amazonaws.com/components/1449/SatCatalog_-_SQUID3_Space_-_SQ-1_Optical_Solar_Reflectors_-_Datasheet.pdf?lastmod=20260119070530",
        "year": 2024,
        "kind": "datasheet",
        "license": "vendor document, linked not reproduced"
      }
    },
    {
      "benchmark": "areal_mass_density",
      "label": "Mass density, SQ-1 rigid OSR",
      "value": 400,
      "bound": "exact",
      "unit": "g/m2",
      "scope": "material",
      "conditions": {
        "product": "SQ-1 Rigid Optical Solar Reflector"
      },
      "method": "Vendor product table, printed as 400 g/m2",
      "status": "ground",
      "source": "squid3-sq1-datasheet",
      "where": "Product table, row SQ-1, column MASS DENSITY",
      "source_detail": {
        "title": "SQ-1 and SQ-2 Optical Solar Reflectors datasheet (SQUID3 Space, Version 2024/10)",
        "id": "SQUID3 datasheet, Version 2024/10; hosted on SatCatalog",
        "url": "https://satcatalog.s3.amazonaws.com/components/1449/SatCatalog_-_SQUID3_Space_-_SQ-1_Optical_Solar_Reflectors_-_Datasheet.pdf?lastmod=20260119070530",
        "year": 2024,
        "kind": "datasheet",
        "license": "vendor document, linked not reproduced"
      }
    },
    {
      "benchmark": "thickness",
      "label": "Thickness, SQ-1 rigid OSR",
      "value": 0.3,
      "bound": "exact",
      "unit": "mm",
      "scope": "material",
      "conditions": {
        "product": "SQ-1 Rigid Optical Solar Reflector"
      },
      "method": "Vendor product table, printed as 0.3 mm",
      "status": "ground",
      "source": "squid3-sq1-datasheet",
      "where": "Product table, row SQ-1, column THICKNESS",
      "source_detail": {
        "title": "SQ-1 and SQ-2 Optical Solar Reflectors datasheet (SQUID3 Space, Version 2024/10)",
        "id": "SQUID3 datasheet, Version 2024/10; hosted on SatCatalog",
        "url": "https://satcatalog.s3.amazonaws.com/components/1449/SatCatalog_-_SQUID3_Space_-_SQ-1_Optical_Solar_Reflectors_-_Datasheet.pdf?lastmod=20260119070530",
        "year": 2024,
        "kind": "datasheet",
        "license": "vendor document, linked not reproduced"
      }
    },
    {
      "benchmark": "thickness",
      "label": "Thickness, SQ-1 as listed in SatCatalog",
      "value": 0.2,
      "value_high": 0.4,
      "bound": "range",
      "unit": "mm",
      "scope": "material",
      "conditions": {
        "product": "SQ-1 Optical Solar Reflectors as listed on SatCatalog (the page does not separate SQ-1 from SQ-2)"
      },
      "method": "Range printed on the SatCatalog details table as 0.2~0.4 mm",
      "status": "ground",
      "source": "satcatalog-osr",
      "where": "Details table, row Thickness",
      "source_detail": {
        "title": "SatCatalog: SQ-1 Optical Solar Reflectors (SQUID3 Space) component page",
        "url": "https://www.satcatalog.com/component/sq-1-optical-solar-reflectors",
        "year": 2026,
        "kind": "web",
        "license": "SatCatalog web page (cited, not reproduced)"
      }
    },
    {
      "benchmark": "areal_mass_density",
      "label": "Mass density limit, SQ-1 as listed in SatCatalog",
      "value": 500,
      "bound": "upper",
      "unit": "g/m^2",
      "scope": "material",
      "conditions": {
        "product": "SQ-1 Optical Solar Reflectors as listed on SatCatalog"
      },
      "method": "Upper limit printed as < 500 g/m^2 on the SatCatalog details table",
      "status": "ground",
      "source": "satcatalog-osr",
      "where": "Details table, row Mass density",
      "source_detail": {
        "title": "SatCatalog: SQ-1 Optical Solar Reflectors (SQUID3 Space) component page",
        "url": "https://www.satcatalog.com/component/sq-1-optical-solar-reflectors",
        "year": 2026,
        "kind": "web",
        "license": "SatCatalog web page (cited, not reproduced)"
      }
    },
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, commercial OSR (one sample)",
      "value": 0.049,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "substrate": "fused silica",
        "condition": "initial, before ultraviolet exposure",
        "sample_count": "one sample only"
      },
      "method": "Laboratory value reported in the 1968 study text, given for comparison with the study's own prepared samples",
      "status": "ground",
      "source": "nasa1968",
      "where": "Section 6.3 (Ultraviolet environmental test results), paragraph on the commercial OSR",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, prepared fused silica OSR before ultraviolet",
      "value": 0.044,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "substrate": "fused silica, prepared samples (average)",
        "condition": "before 500 equivalent sun-hour ultraviolet exposure at 700 K"
      },
      "method": "Average of prepared samples as printed in the text; the study says the grades of fused silica did not differ significantly",
      "status": "ground",
      "source": "nasa1968",
      "where": "Section 6.3, paragraph on prepared test samples",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, prepared fused silica OSR after ultraviolet",
      "value": 0.054,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "substrate": "fused silica, prepared samples (average)",
        "condition": "after 500 equivalent sun-hour ultraviolet exposure at 700 K"
      },
      "method": "Average of prepared samples as printed in the text (changed from 0.044 to 0.054)",
      "status": "ground",
      "source": "nasa1968",
      "where": "Section 6.3, paragraph on prepared test samples",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "total_hemispherical_emittance",
      "label": "Total hemispherical emittance, fused silica OSR at 300 K",
      "value": 0.8,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "substrate": "fused silica with vacuum-deposited silver, second surface",
        "temperature": "300 K"
      },
      "method": "Value quoted in the text of Section 7.2 as printed 0.80; the report's summary says emittance was measured from 400 to 800 K, so this 300 K figure is a text statement",
      "status": "ground",
      "note": "Printed as 0.80 in the report text",
      "source": "nasa1968",
      "where": "Section 7.2 (Emittance relationships), page 7-2",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "total_hemispherical_emittance",
      "label": "Total hemispherical emittance, fused silica OSR at 750 K",
      "value": 0.67,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "substrate": "fused silica with vacuum-deposited silver, second surface",
        "temperature": "750 K"
      },
      "method": "Value quoted in the text of Section 7.2, as the endpoint of a decrease from 0.80 at 300 K",
      "status": "ground",
      "source": "nasa1968",
      "where": "Section 7.2 (Emittance relationships), page 7-2",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, 210 A alumina over silver, before exposure",
      "value": 0.055,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "coating": "210 A alumina overcoat on 1200 A silver on fused silica substrate",
        "state": "before hydrogen sulfide exposure"
      },
      "method": "Measured value in Table 6-1 (accelerated corrosion test)",
      "status": "ground",
      "source": "nasa1968",
      "where": "Table 6-1 (Corrosion of alumina overcoated silver), 210 A row, Before Exposure column",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, 210 A alumina over silver, after 1 h",
      "value": 0.064,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "coating": "210 A alumina overcoat on 1200 A silver on fused silica substrate",
        "exposure": "1 h in hydrogen sulfide vapour (ammonium polysulfide, near 100% relative humidity)"
      },
      "method": "Measured value in Table 6-1 (accelerated corrosion test)",
      "status": "ground",
      "source": "nasa1968",
      "where": "Table 6-1, 210 A row, After 1 hr Exposure column",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, 550 A alumina over silver, before exposure",
      "value": 0.054,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "coating": "550 A alumina overcoat on 1200 A silver on fused silica substrate",
        "state": "before hydrogen sulfide exposure"
      },
      "method": "Measured value in Table 6-1 (accelerated corrosion test)",
      "status": "ground",
      "source": "nasa1968",
      "where": "Table 6-1, 550 A row, Before Exposure column",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, 550 A alumina over silver, after 1 h",
      "value": 0.06,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "coating": "550 A alumina overcoat on 1200 A silver on fused silica substrate",
        "exposure": "1 h in hydrogen sulfide vapour (ammonium polysulfide, near 100% relative humidity)"
      },
      "method": "Measured value in Table 6-1 (accelerated corrosion test)",
      "status": "ground",
      "source": "nasa1968",
      "where": "Table 6-1, 550 A row, After 1 hr Exposure column",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, 955 A alumina over silver, before exposure",
      "value": 0.054,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "coating": "955 A alumina overcoat on 1200 A silver on fused silica substrate",
        "state": "before hydrogen sulfide exposure"
      },
      "method": "Measured value in Table 6-1 (accelerated corrosion test)",
      "status": "ground",
      "source": "nasa1968",
      "where": "Table 6-1, 955 A row, Before Exposure column",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "solar_absorptance",
      "label": "Solar absorptance, 955 A alumina over silver, after 1 h",
      "value": 0.059,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "coating": "955 A alumina overcoat on 1200 A silver on fused silica substrate",
        "exposure": "1 h in hydrogen sulfide vapour (ammonium polysulfide, near 100% relative humidity)"
      },
      "method": "Measured value in Table 6-1 (accelerated corrosion test)",
      "status": "ground",
      "source": "nasa1968",
      "where": "Table 6-1, 955 A row, After 1 hr Exposure column",
      "source_detail": {
        "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
        "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
        "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
        "year": 1968,
        "kind": "report",
        "license": "public domain (NASA)"
      }
    },
    {
      "benchmark": "density",
      "label": "Density, fused silica substrate",
      "value": 2.2,
      "bound": "exact",
      "unit": "g/cm3",
      "scope": "material",
      "conditions": {
        "temperature": "not stated on the page"
      },
      "method": "Printed as 2.20 g/cm3 in the Fused Silica Properties table; describes the substrate, not the OSR stack",
      "status": "ground",
      "source": "pmoptics-fused-silica",
      "where": "Fused Silica Properties table, row Density",
      "source_detail": {
        "title": "Fused Silica, PMOptics property page (Fused Silica Properties table and refractive index table)",
        "url": "https://www.pmoptics.com/Fused_Silica.html",
        "kind": "web",
        "license": "supplier web page (cited, not reproduced)"
      }
    },
    {
      "benchmark": "thermal_conductivity",
      "label": "Thermal conductivity, fused silica substrate",
      "value": 1.4,
      "bound": "exact",
      "unit": "W/m·°C",
      "scope": "material",
      "conditions": {
        "temperature": "not stated on the page"
      },
      "method": "Printed in the Fused Silica Properties table",
      "status": "ground",
      "source": "pmoptics-fused-silica",
      "where": "Fused Silica Properties table, row Thermal Conductivity",
      "source_detail": {
        "title": "Fused Silica, PMOptics property page (Fused Silica Properties table and refractive index table)",
        "url": "https://www.pmoptics.com/Fused_Silica.html",
        "kind": "web",
        "license": "supplier web page (cited, not reproduced)"
      }
    },
    {
      "benchmark": "refractive_index",
      "label": "Refractive index, fused silica substrate",
      "value": 1.45702,
      "bound": "exact",
      "unit": "-",
      "scope": "material",
      "conditions": {
        "wavelength": "0.633 µm (633 nm)",
        "temperature": "not stated on the page"
      },
      "method": "Printed in the refractive index table at 0.633 um",
      "status": "ground",
      "source": "pmoptics-fused-silica",
      "where": "Refractive Index table, row 0.633 um",
      "source_detail": {
        "title": "Fused Silica, PMOptics property page (Fused Silica Properties table and refractive index table)",
        "url": "https://www.pmoptics.com/Fused_Silica.html",
        "kind": "web",
        "license": "supplier web page (cited, not reproduced)"
      }
    }
  ],
  "corrosion": [
    {
      "environment": "Hydrogen sulfide vapour with near 100% relative humidity (accelerated test; ammonium polysulfide in a closed container)",
      "headline": "A bare silver film blackened within a fraction of a second in the 1968 test.",
      "effect": "The report says this test is probably one of the most rigorous for silver films, and that a bare silver film blackened in a fraction of a second. Table 6-1 has one row marked film failure, with absorptance rising from 0.047 to 0.677; the text layer does not print that row's coating, so it is not used here as a bare-silver value.",
      "rating": "severe",
      "conditions": {
        "exposure": "closed container, hydrogen sulfide from ammonium polysulfide, near 100% relative humidity",
        "coating": "bare silver film (one row of Table 6-1 marked film failure)"
      },
      "source": "nasa1968",
      "where": "Section 6.2 (silver film stability), discussion before Table 6-1"
    },
    {
      "environment": "Hydrogen sulfide vapour with near 100% relative humidity, 1 h (alumina overcoated silver)",
      "headline": "Alumina overcoats kept silver usable in the same test: solar absorptance rose from 0.055 to 0.064 with 210 A alumina.",
      "effect": "Table 6-1 gives absorptance before and after one hour for 210 A alumina (0.055 to 0.064), 550 A (0.054 to 0.060) and 955 A (0.054 to 0.059) over 1200 A silver on fused silica. The conclusions say alumina of at least 500 A is very acceptable, and that in a corrosive environment the attack starts at the exposed substrate edge.",
      "rating": "low",
      "conditions": {
        "exposure": "1 h, closed container, hydrogen sulfide from ammonium polysulfide",
        "coating": "1200 A silver on fused silica with 210, 550 or 955 A alumina"
      },
      "source": "nasa1968",
      "where": "Table 6-1 and Section 8.1 (film deposition, corrosion resistance)"
    },
    {
      "environment": "Ultraviolet, 500 equivalent sun-hours at 700 K (fused silica substrates)",
      "headline": "Ultraviolet at 700 K raised solar absorptance only slightly, by about 1%.",
      "effect": "The report says the OSRs showed a small increase in solar absorptance after the ultraviolet test, which it traced to a change in the transmittance of the fused silica (about 1%). Grades of fused silica did not differ significantly. Prepared samples changed from 0.044 to 0.054 on average; one commercial OSR sample, at 0.049, did not change.",
      "rating": "low",
      "conditions": {
        "dose": "500 equivalent sun-hours",
        "temperature": "700 K",
        "substrates": "Suprasil 11, Spectrasil B, Corning 7940 (industrial and UV grade) and G.E. 151 fused silica"
      },
      "source": "nasa1968",
      "where": "Section 6.3 (Ultraviolet environmental test results) and Section 8.3 (OSR ultraviolet exposure)"
    },
    {
      "environment": "2 keV protons, up to 5 x 10^17 p/cm2, substrate temperatures of 400, 530 and 700 K",
      "headline": "No optical damage was seen in the fused silica OSRs under these proton exposures.",
      "effect": "The report says none of the samples showed optical damage, and that fused silica showed no change in solar absorptance after the highest proton dose at 700 K, whatever its grade or source. The report also checked the stability of the coating system's spectral reflectance after exposure.",
      "rating": "none",
      "conditions": {
        "energy": "2 keV protons",
        "dose": "up to 5 x 10^17 p/cm2",
        "temperature": "400, 530 and 700 K"
      },
      "source": "nasa1968",
      "where": "Section 6.4 (Proton radiation test results) and Section 8.2 (Proton environment)"
    },
    {
      "environment": "Thermal vacuum cycling from -40 °C to +120 °C (manufacturer claim)",
      "headline": "SQUID3 says the SQ-1 passes thermal vacuum cycling from -40 °C to +120 °C; no test report was read.",
      "effect": "The datasheet lists this among its features. No cycle count, test report or before-and-after optical values are printed, so this is a vendor claim only.",
      "rating": "unknown",
      "conditions": {
        "basis": "vendor features list",
        "products": "SQ-1 and SQ-2"
      },
      "source": "squid3-sq1-datasheet",
      "where": "Features list"
    }
  ],
  "risks": {
    "hazards": [
      {
        "text": "PubChem lists vitreous silica (EC 262-373-8) as Not Classified under GHS, aggregated over 1682 reports by companies from 17 notifications to the ECHA C&L Inventory.",
        "ghs": [],
        "source": "pubchem-silica-ghs",
        "where": "Safety and Hazards, GHS Classification, ECHA entry 'Silica, vitreous (EC: 262-373-8)' (CID 24261)"
      },
      {
        "text": "Other silica forms on the same PubChem record are classified, so the substance name matters: amorphous silica (EC 601-216-3) carries Warning with H315 (56.3%), H319 (56.3%) and H335 (56.3%), aggregated over 2540 reports; cristobalite (EC 238-455-4) carries Danger with H350 (12.6%): May cause cancer.",
        "ghs": [
          "H315",
          "H319",
          "H335",
          "H350"
        ],
        "source": "pubchem-silica-ghs",
        "where": "Safety and Hazards, GHS Classification, ECHA entries 'AMORPHOUS SILICA (EC: 601-216-3)' and 'Cristobalite (EC: 238-455-4)' (CID 24261)"
      },
      {
        "text": "PubChem gives the main ECHA entry for silver (EC 231-131-3) as Warning with H400 (70.4%): Very toxic to aquatic life, aggregated over 2154 reports by companies from 36 notifications.",
        "ghs": [
          "H400"
        ],
        "source": "pubchem-silver-ghs",
        "where": "Safety and Hazards, GHS Classification, ECHA entry 'Silver (EC: 231-131-3)' (CID 23954)"
      },
      {
        "text": "PubChem lists a revised classification for silver (excluding nanoparticles), FY2022, as Danger with H360: May damage fertility or the unborn child.",
        "ghs": [
          "H360"
        ],
        "source": "pubchem-silver-ghs",
        "where": "Safety and Hazards, GHS Classification, entry 'Silver (excluding nanoparticles) - FY2022 (Revised classification)' (CID 23954)"
      }
    ],
    "failure_risks": [
      {
        "mode": "Corrosion of an unprotected silver film",
        "trigger": "Humid, sulfur-bearing air (hydrogen sulfide vapour in the 1968 accelerated test)",
        "consequence": "The report says a bare silver film blackened in a fraction of a second. The silver is what gives the OSR its low solar absorptance.",
        "severity": "high",
        "source": "nasa1968",
        "where": "Section 6.2 (silver film stability), discussion before Table 6-1"
      },
      {
        "mode": "Attack from exposed substrate edges",
        "trigger": "A corrosive environment reaching the uncovered edge of the coating",
        "consequence": "The report says in a corrosive environment the attack starts at the exposed substrate edge.",
        "severity": "moderate",
        "source": "nasa1968",
        "where": "Section 8.1 (film deposition conclusions)"
      },
      {
        "mode": "Rise in solar absorptance after ultraviolet exposure",
        "trigger": "500 equivalent sun-hours of ultraviolet at 700 K",
        "consequence": "Solar absorptance rose by about 1%, which the report traces to a change in transmittance of the fused silica.",
        "severity": "low",
        "source": "nasa1968",
        "where": "Section 8.3 (OSR ultraviolet exposure)"
      }
    ],
    "side_effects": [
      {
        "text": "Emittance falls as the surface warms, from 0.80 at 300 K to 0.67 at 750 K.",
        "affects": "Radiator heat rejection at high surface temperature",
        "source": "nasa1968",
        "where": "Section 7.2 (Emittance relationships), page 7-2"
      }
    ],
    "handling": [
      {
        "text": "The report's preparation used a mild hydrofluoric substrate etch, then heating the substrate to about 500 K before vacuum deposition, for silver adhesion. The report says this treatment did not change solar absorptance.",
        "source": "nasa1968",
        "where": "Section 8.1 (film deposition)"
      }
    ],
    "mitigations": [
      {
        "text": "Overcoat the silver with alumina of at least 500 A; the report's conclusions call this minimum very acceptable for corrosion resistance in its hydrogen sulfide test.",
        "source": "nasa1968",
        "where": "Section 8.1 (film deposition)"
      }
    ]
  },
  "uses": [
    {
      "application": "thermal-control",
      "device": "Satellite radiator surfaces (second-surface mirror)",
      "example": "The NASA 1968 study defines an optical solar reflector as a second surface mirror of silver on a fused silica substrate, for low solar absorptance and a low ratio of solar absorptance to infrared emittance.",
      "source": "nasa1968",
      "where": "Section 2 (program objectives), definition of OSR"
    },
    {
      "application": "thermal-control",
      "device": "Commercial rigid OSR tile (SQUID3 SQ-1)",
      "example": "SQUID3 says the SQ-1 may be used as a surface material on satellite radiators and structural panels, with standard sizes of 1 x 1 in and 2 x 2 in.",
      "source": "squid3-sq1-datasheet",
      "where": "Applications section and product standard sizes"
    },
    {
      "application": "thermal-control",
      "device": "Thermal subsystem component (SQ-1 listing)",
      "example": "SatCatalog lists the SQ-1 under the Thermal Subsystem, with component type Optical Solar Reflectors and status In Production.",
      "source": "satcatalog-osr",
      "where": "Overview table, Subsystem, Component Type and Status rows"
    }
  ],
  "supply": [
    {
      "subject": "Silver (reflective layer)",
      "producers": [
        {
          "country": "Mexico",
          "share_percent": 24.2,
          "year": 2025
        },
        {
          "country": "Peru",
          "share_percent": 13.8,
          "year": 2025
        },
        {
          "country": "China",
          "share_percent": 13.1,
          "year": 2025
        }
      ],
      "critical_lists": [
        {
          "list": "USGS 2025 Final List of Critical Minerals (silver added in the 2025 list)",
          "listed": true
        }
      ],
      "recycling": "USGS: about 1,000 tons of silver was recovered from new and old scrap in the United States in 2025, about 11% of apparent consumption.",
      "substitutes": [
        "USGS lists substitutes for photographic, surgical, flatware and some battery uses; it does not discuss mirror coatings."
      ],
      "source": "usgs-mcs2026-silver",
      "where": "World Mine Production and Reserves table, 2025e column (world total 26,000 t; shares calculated by Space Mushroom against that total); Recycling; Substitutes; critical list statement"
    },
    {
      "subject": "Silicon (fused silica substrate)",
      "producers": [
        {
          "country": "China",
          "share_percent": 87,
          "year": 2025
        },
        {
          "country": "Brazil",
          "share_percent": 3.9,
          "year": 2025
        },
        {
          "country": "Norway",
          "share_percent": 2.8,
          "year": 2025
        },
        {
          "country": "Russia",
          "share_percent": 0.8,
          "year": 2025
        }
      ],
      "critical_lists": [
        {
          "list": "USGS 2025 Final List of Critical Minerals (silicon added in the 2025 list)",
          "listed": true
        }
      ],
      "recycling": "USGS silicon chapter: recycling is \"Insignificant.\"",
      "substitutes": [
        "USGS silicon chapter: gallium arsenide and germanium are the principal substitutes for silicon in semiconductor and infrared applications."
      ],
      "source": "usgs-mcs2026-silicon",
      "where": "World Production table, silicon metal, 2025 column (thousand metric tons, silicon content; world total 4,600 printed as rounded; shares calculated by Space Mushroom against that total). The chapter's world-resources statement names silica in natural forms, such as quartzite, as the source of silicon. This is a silicon-metal statistic, not a fused-silica production figure; none was found."
    }
  ],
  "media": [],
  "documents": [
    {
      "title": "SQ-1 and SQ-2 Optical Solar Reflectors datasheet (SQUID3 Space, Version 2024/10)",
      "type": "datasheet",
      "url": "https://satcatalog.s3.amazonaws.com/components/1449/SatCatalog_-_SQUID3_Space_-_SQ-1_Optical_Solar_Reflectors_-_Datasheet.pdf?lastmod=20260119070530",
      "year": 2024
    },
    {
      "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Lockheed final report 4-06-68-1, NASA NTRS 19680015854)",
      "type": "report",
      "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
      "year": 1968
    },
    {
      "title": "Mineral Commodity Summaries 2026: Silver",
      "type": "report",
      "url": "https://pubs.usgs.gov/periodicals/mcs2026/mcs2026-silver.pdf",
      "year": 2026
    },
    {
      "title": "NIST Atomic Weights and Isotopic Compositions: silicon",
      "type": "database",
      "url": "https://physics.nist.gov/cgi-bin/Compositions/stand_alone.pl?ele=Si&all=all&ascii=html"
    },
    {
      "title": "Mineral Commodity Summaries 2026: Silicon",
      "type": "report",
      "url": "https://pubs.usgs.gov/periodicals/mcs2026/mcs2026-silicon.pdf",
      "year": 2026
    },
    {
      "title": "PubChem: Silica (CID 24261), GHS classification (ECHA notifications)",
      "type": "database",
      "url": "https://pubchem.ncbi.nlm.nih.gov/compound/24261",
      "year": 2026
    },
    {
      "title": "PubChem: Silver (CID 23954), GHS classification (ECHA notifications)",
      "type": "database",
      "url": "https://pubchem.ncbi.nlm.nih.gov/compound/23954",
      "year": 2026
    }
  ],
  "gaps": [
    "No flight, thermal-vacuum or on-orbit test data for an OSR found in the sources read; the 1968 results are laboratory measurements and the SQ-1 thermal-vacuum claim has no test report.",
    "The SQUID3 datasheet and SatCatalog page do not name the substrate of the SQ-1; the 1968 fused silica design is not assumed to be the SQ-1 construction. The SQ-1 areal mass and thickness are not used to infer a material.",
    "SatCatalog lists the form factor of the same product as both All and Rigid/Flexible; the datasheet lists SQ-1 as Rigid and SQ-2 as Flexible.",
    "Solar absorptance and infrared emittance from SQUID3 carry no unit and no test method; recorded as dimensionless with the caveat in method.",
    "The 1968 report gives OSR emittance at 300 K and 750 K only in the text (0.80 and 0.67); the emittance figures (Figs. 6-1 to 6-4) and the full temperature curve were not read in this run.",
    "Table 6-2 (solar absorptance after ultraviolet, by grade) is not legible in the text layer; only the text averages are used.",
    "The Table 6-1 row marked film failure has no legible coating label, so it is not used as a bare-silver absorptance value.",
    "Hazard data come from PubChem ECHA notification summaries only; no safety data sheet for silver or vitreous silica was read in this run, and the PubChem entries are aggregated company reports, not a single product classification.",
    "Outgassing: SQUID3 claims a low outgassing requirement (ASTM E-595) but prints no total mass loss or collected volatile condensable material values.",
    "Silicon production shares are from the silicon-metal table, not from fused-silica feedstock; no fused-silica or quartz-glass production statistic was found. Silver EU critical raw materials status was not read in this run.",
    "Refractive index was read at one wavelength (0.633 um) from the pmoptics table; no temperature dependence was printed.",
    "No images were fetched or read; no media entries."
  ],
  "story": {
    "why": "An optical solar reflector (OSR) is a mirror that reflects sunlight while letting a spacecraft radiator shed its own heat. The 1968 Lockheed study for NASA defined the OSR as a second-surface silver mirror on a fused silica substrate, and this profile covers that design. Modern rigid OSR tiles, such as SQUID3's SQ-1, are sold for satellite radiators, but their datasheet does not name the substrate.",
    "uses": [
      {
        "where": "Satellite radiators (1968 NASA definition)",
        "line": "The 1968 study defined the OSR as a second-surface silver mirror on a fused silica substrate, for low solar absorptance and a low ratio of solar absorptance to infrared emittance."
      },
      {
        "where": "Commercial rigid OSR tile",
        "line": "SQUID3 sells the SQ-1 for satellite radiators and structural panels, in standard sizes of 1 x 1 in and 2 x 2 in."
      }
    ],
    "can_do": [
      {
        "label": "Low solar absorptance",
        "line": "A commercial OSR sample read 0.049 in the 1968 study. Prepared fused silica OSRs averaged 0.044 before ultraviolet exposure and 0.054 after. SQUID3 prints 0.1 for the SQ-1. Each figure carries its own test conditions in the properties.",
        "benchmark": "solar_absorptance",
        "scope": "material"
      },
      {
        "label": "High infrared emittance",
        "line": "SQUID3 prints an infrared emittance above 0.8 for the SQ-1, written as '> 0.8'. The 1968 study printed a total hemispherical emittance of 0.80 at 300 K for the fused silica OSR.",
        "benchmark": "infrared_emittance",
        "scope": "material"
      },
      {
        "label": "Emittance with temperature",
        "line": "According to the 1968 report text, emittance falls as the surface warms, from 0.80 at 300 K to 0.67 at 750 K.",
        "benchmark": "total_hemispherical_emittance",
        "scope": "material",
        "value": "0.80 at 300 K to 0.67 at 750 K"
      },
      {
        "label": "Corrosion protection",
        "line": "In the same hydrogen sulfide test, 210 A alumina over silver moved from 0.055 to 0.064 in one hour, while a bare silver film blackened within a fraction of a second.",
        "benchmark": "solar_absorptance",
        "scope": "material"
      },
      {
        "label": "Thermal vacuum cycling",
        "line": "SQUID3 claims the SQ-1 passes thermal vacuum cycling from -40 °C to +120 °C. This is a vendor claim with no test report read.",
        "scope": "material",
        "value": "-40 °C to +120 °C"
      }
    ],
    "compare": "Among the figures in this profile, the 1968 fused silica OSR is the measured reference: solar absorptance 0.044 before and 0.054 after ultraviolet exposure, against 0.049 for one commercial OSR sample. Against a bare silver film, which blackened within a fraction of a second in the hydrogen sulfide test, alumina-overcoated silver stayed at 0.064 after one hour with 210 A alumina. The SQ-1 datasheet prints a solar absorptance of 0.1, which is higher than the 1968 samples, but it gives no test method or substrate, so the two cannot be compared directly.",
    "compare_rows": [
      {
        "label": "Solar absorptance (lower is better)",
        "benchmark": "solar_absorptance",
        "scope": "material"
      },
      {
        "label": "Infrared emittance (higher is better)",
        "benchmark": "infrared_emittance",
        "scope": "material"
      },
      {
        "label": "Total hemispherical emittance at 300 K and 750 K",
        "benchmark": "total_hemispherical_emittance",
        "scope": "material"
      }
    ],
    "handling": [
      "Keep the silver away from sulfur-bearing humid air. A bare silver film blackened within a fraction of a second in the 1968 test.",
      "Overcoat the silver with alumina of at least 500 A. The 1968 conclusions call this minimum very acceptable.",
      "For silver adhesion, the 1968 preparation etched the substrate with a mild hydrofluoric acid treatment and then heated it to about 500 K before deposition."
    ],
    "good_for": [
      "Radiator surfaces that need low solar absorptance with high infrared emittance. The 1968 OSR had 0.044 to 0.054 solar absorptance, and SQUID3 prints 0.1 with an infrared emittance above 0.8 for the SQ-1.",
      "Thermal control in sunlight. The 1968 study states its purpose as low solar absorptance and a low ratio of absorptance to emittance."
    ],
    "watch_out": [
      "Bare silver corrodes in sulfur-bearing humid air. In the 1968 test, the alumina overcoat was what protected it.",
      "Emittance falls as the surface warms, from 0.80 at 300 K to 0.67 at 750 K.",
      "Solar absorptance rose after ultraviolet exposure, by about 1% in the report, from 0.044 to 0.054 on average for prepared samples.",
      "The SQ-1 datasheet does not name its substrate or test method, so its figures cannot be taken as fused silica data."
    ],
    "verdict": "A fused silica OSR is a well-documented low-absorptance, high-emittance radiator surface, with measured data on corrosion, ultraviolet and proton exposure from a 1968 study prepared for NASA. The modern SQ-1 product sheet has catalogued figures only, with no named substrate or test method, so the 1968 fused silica design holds the measured detail.",
    "recipe": {
      "line": "The fused silica substrate is made of silicon and oxygen. The reflective layer is vacuum-deposited silver on its back surface, and the 1968 test samples added an optional alumina (aluminium oxide) overcoat on top of the silver.",
      "parts": [
        {
          "name": "Silicon",
          "symbol": "Si",
          "role": "Main element of the fused silica substrate. Its atomic weight is given as [28.084, 28.086] in the identity note (NIST)."
        },
        {
          "name": "Oxygen",
          "symbol": "O",
          "role": "Second element of the fused silica substrate. Its atomic weight is given as [15.999 03, 15.999 77] in the identity note (NIST)."
        },
        {
          "name": "Silver",
          "symbol": "Ag",
          "role": "The second-surface mirror. Silver reflects sunlight, and the 1968 samples used 1200 A of it on fused silica."
        },
        {
          "name": "Alumina (aluminium oxide)",
          "symbol": "Al₂O₃",
          "role": "Optional overcoat over the silver, which the 1968 study tested at 210, 550 and 955 A to protect it from corrosion."
        }
      ]
    },
    "risk_groups": [
      {
        "title": "For people",
        "lead": "PubChem summarizes ECHA notifications for these materials. Vitreous silica is listed as Not Classified. Silver is listed with H400 (very toxic to aquatic life), and a revised FY2022 entry lists H360 (may damage fertility or the unborn child).",
        "points": [
          {
            "label": "Silica",
            "line": "Vitreous silica (EC 262-373-8) is listed as Not Classified. Other silica forms on the same PubChem record are classified, so the form matters."
          },
          {
            "label": "Silver",
            "line": "The main ECHA entry for silver (EC 231-131-3) carries H400. A revised classification for silver, excluding nanoparticles, carries Danger with H360."
          },
          {
            "label": "Data limits",
            "line": "These are aggregated company notifications, not a product safety data sheet. No safety data sheet for the OSR was read."
          }
        ],
        "level": 0,
        "verdict": "Mixed: silica not classified, silver classified"
      },
      {
        "title": "If the coating is damaged",
        "lead": "The 1968 study tested the failure mode that matters most for silver: sulfur-bearing humid air.",
        "points": [
          {
            "label": "Bare silver",
            "line": "In the hydrogen sulfide test, the report says a bare silver film blackened within a fraction of a second."
          },
          {
            "label": "Edges",
            "line": "In a corrosive environment the attack starts at the exposed substrate edge, according to the report's conclusions."
          }
        ]
      },
      {
        "title": "Handling and storage",
        "points": [
          {
            "label": "Preparation",
            "line": "The report's preparation used a mild hydrofluoric etch of the substrate, then heating to about 500 K before deposition. This profile records no safety data for hydrofluoric acid."
          }
        ]
      }
    ]
  },
  "updated": "2026-11-01",
  "review": {
    "status": "draft",
    "method": "assistant",
    "checked_values": 20,
    "unreachable": 0,
    "caveats": 3,
    "note": "Read by an AI assistant on 2026-11-01: SatCatalog page, SQUID3 SQ-1 datasheet, NASA 1968 report (text layer and Table 6-1), USGS silver and silicon chapters, PMOptics fused silica table, NIST atomic weights, PubChem silica and silver GHS records (read through the PubChem JSON view, since the web pages returned a browser check)."
  },
  "sources": {
    "satcatalog-osr": {
      "title": "SatCatalog: SQ-1 Optical Solar Reflectors (SQUID3 Space) component page",
      "url": "https://www.satcatalog.com/component/sq-1-optical-solar-reflectors",
      "year": 2026,
      "kind": "web",
      "license": "SatCatalog web page (cited, not reproduced)"
    },
    "squid3-sq1-datasheet": {
      "title": "SQ-1 and SQ-2 Optical Solar Reflectors datasheet (SQUID3 Space, Version 2024/10)",
      "id": "SQUID3 datasheet, Version 2024/10; hosted on SatCatalog",
      "url": "https://satcatalog.s3.amazonaws.com/components/1449/SatCatalog_-_SQUID3_Space_-_SQ-1_Optical_Solar_Reflectors_-_Datasheet.pdf?lastmod=20260119070530",
      "year": 2024,
      "kind": "datasheet",
      "license": "vendor document, linked not reproduced"
    },
    "nasa1968": {
      "title": "Low Solar Absorptance and Emittance Surfaces Utilizing Vacuum Deposited Techniques (Greenberg and Vance, Lockheed Palo Alto Research Laboratory, final report 4-06-68-1)",
      "id": "NASA NTRS 19680015854; Lockheed report 4-06-68-1; contract NAS 2-3063",
      "url": "https://ntrs.nasa.gov/api/citations/19680015854/downloads/19680015854.pdf",
      "year": 1968,
      "kind": "report",
      "license": "public domain (NASA)"
    },
    "pmoptics-fused-silica": {
      "title": "Fused Silica, PMOptics property page (Fused Silica Properties table and refractive index table)",
      "url": "https://www.pmoptics.com/Fused_Silica.html",
      "kind": "web",
      "license": "supplier web page (cited, not reproduced)"
    },
    "usgs-mcs2026-silver": {
      "title": "Mineral Commodity Summaries 2026, Silver",
      "id": "USGS MCS 2026, February 2026",
      "url": "https://pubs.usgs.gov/periodicals/mcs2026/mcs2026-silver.pdf",
      "year": 2026,
      "kind": "report",
      "license": "public domain (USGS)"
    },
    "nist-atomic-weights": {
      "title": "NIST Atomic Weights and Isotopic Compositions for Silicon and Oxygen",
      "id": "NIST Standard Reference Data, stand-alone compositions pages (Si, O)",
      "url": "https://physics.nist.gov/cgi-bin/Compositions/stand_alone.pl?ele=Si&all=all&ascii=html",
      "kind": "database",
      "license": "public domain (NIST)"
    },
    "usgs-mcs2026-silicon": {
      "title": "Mineral Commodity Summaries 2026, Silicon",
      "id": "USGS MCS 2026, February 2026",
      "url": "https://pubs.usgs.gov/periodicals/mcs2026/mcs2026-silicon.pdf",
      "year": 2026,
      "kind": "report",
      "license": "public domain (USGS)"
    },
    "pubchem-silica-ghs": {
      "title": "PubChem: Silica (CID 24261), Safety and Hazards, GHS Classification",
      "id": "PubChem CID 24261 (ECHA C&L Notifications Summary)",
      "url": "https://pubchem.ncbi.nlm.nih.gov/compound/24261",
      "year": 2026,
      "kind": "database",
      "license": "PubChem record (cited, not reproduced)"
    },
    "pubchem-silver-ghs": {
      "title": "PubChem: Silver (CID 23954), Safety and Hazards, GHS Classification",
      "id": "PubChem CID 23954 (ECHA C&L Notifications Summary)",
      "url": "https://pubchem.ncbi.nlm.nih.gov/compound/23954",
      "year": 2026,
      "kind": "database",
      "license": "PubChem record (cited, not reproduced)"
    }
  },
  "license": "CC-BY-4.0",
  "url": "https://spacemushroom.com/profiles/fused-silica-optical-solar-reflector/"
}